MECHANICAL WORKS stamping chains tube spring
CASTING closed systems open systems. Not for casting in Place.
Density: 14.60 g/cmᶟHardness (as cast): 170 HV
Hardness (after cold work 70%): 271 HV
Hardness (after annealing): 168 HV
Hardness (after age hardening): 300 HV
DIRECTIONS FOR SUGGESTED USE
Melting temperature: 910 °C
Casting temperature:
100 °C over its melting temperature to cast into ingot-mould and continuous casting
100 °C over its melting temperature to cast with centrifugal machines
120 °C over its melting temperature to cast in vacuum machines with controlled atmosphere
140 °C over its melting temperature to cast in outdoor cylinders with vacuum
Ingot-mould temperature: 150 °C
Cylinders temperature: from 550 °C to 650 °C depending on the machine and
objects dimensions
Cooling of ingots: quick in lukewarm water (about 40 °C)
Cooling casted objects: in water after 10 minutes
Annealing: 650 °C for 20 minutes followed by a quick cooling in hot
water (40 °C min.)
Age hardening: Step 1: solubilization
680 °C for 30 minutes. Cooling quickly in warm water (about
40 °C).
Step 2: hardening
300 °C for 2 hours. Cooling at room temperature.